Process for forming an ultra fine pattern using a bottom anti-reflective coating film containing an acid generator

ABSTRACT

A process of forming ultra fine patterns using bottom anti-reflective coating containing acid generator. More particularly, a process of forming vertical patterns using an organic bottom anti-reflective coating containing excessive amount of acid generator, in order to prevent formation of sloping patterns due to photoresist resins absorbing wavelength of light used as light sources during lithography process using light sources such as KrF, ArF, VUV, EUV, E-beam and ion beam, even when photoresist resins having high absorbance to light source are used.

BACKGROUND

[0001] 1. Technical Field

[0002] A process for forming ultra fine patterns using a bottom anti-reflective coating film containing an acid generator is disclosed. More specifically, a process for forming vertical patterns is disclosed that uses an organic bottom anti-reflective coating film containing excessive amount of an acid generator in order to prevent formation of sloping patterns due to the photoresist resins absorbing light of wavelength used as the light source, even when photoresist resins having a high absorbance to light source are utilized.

[0003] 2. Description of the Related Art

[0004] A fine circuit of 150 nm L/S has been formed in a process of manufacturing semiconductor fine circuits using KrF of 248 nm, and an attempt has been recently made to form patterns of 150 nm or less. Further, a study on the process of manufacturing fine circuits using light sources having low wavelength such as ArF(193 nm), VUV(157 nm) and EUV(Extremely Ultraviolet; 13 nm) is underway.

[0005] However, it is difficult to develop photoresist resins having high permeability to these wavelengths. Because photoresist used in i-line(365 nm) and KrF(248 nm), wherein its resins consist of aromatic compounds, has high absorbance at the wavelength of 193 nm, the photoresist may not used in 193 nm wavelength. Therefore, photoresist for 193 nm wavelength is developing by using acrylic and alicyclic resins having no aromatic compound. Here, it is difficult to form good patterns because these resins have high absorbance to 193 nm wavelength.

[0006]FIG. 1a is a cross sectional view of the vertical pattern formed after development when a coated photoresist composition has low light absorbance. The amount of light reached on the upper portion of a photoresist 12 coated on an underlying layer 10 is approximately equivalent to the lower portion of a photoresist 12. As a result, vertical patterns 14 may be formed. However, when a chemically amplified photoresist is used, sloping patterns 18 is formed since more light exposure is performed on the upper portions of the photoresist 16 relative to the lower portion of the photoresist 16 (See FIG. 1b). In other words, sloping patterns may be formed because concentration gradient of acid generated by exposure is different according to the height in a vertical direction.

[0007] Although most studies have placed importance on developing resins having low absorbance to light source, this resin development has reached the limits when light sources such as VUV(157 nm) or EUV(13 nm) are used.

SUMMARY OF THE DISCLOSURE

[0008] Accordingly, a bottom anti-reflective coating film comprising an acid generator is disclosed to obtain vertical patterns when photoresist resins have high absorbance to light source.

[0009] A process for forming patterns which uses the bottom anti-reflective film is also disclosed.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010]FIG. 1a is a cross sectional view of the vertical pattern formation when a coated photoresist composition has low light absorbance.

[0011]FIG. 1b is a cross sectional view of the sloping pattern formation when the coated photoresist composition has high light absorbance.

[0012]FIG. 1c is a cross sectional view of the pattern formation obtained in the present invention.

[0013]FIG. 2 shows a pattern obtained in Example 9.

[0014]FIG. 3 shows a pattern obtained in Example 10.

[0015]FIG. 4 shows a pattern obtained in Example 11.

[0016]FIG. 5 shows a pattern obtained in Example 12.

[0017]FIG. 6 shows a pattern obtained in Example 13.

[0018]FIG. 7 shows a pattern obtained in Example 14.

[0019]FIG. 8 shows a pattern obtained in Example 16.

[0020]FIG. 9 shows a pattern obtained in Comparative Example.

DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMBODIMENTS

[0021] A process of forming photoresist patterns is disclosed which uses a bottom anti-reflective coating composition comprising an excessive amount of acid generator.

[0022] A disclosed process for forming patterns comprises: (a) forming a bottom anti-reflective coating film by coating and baking a bottom anti-reflective coating composition on an underlying layer; (b) forming a photoresist film by coating and baking a photoresist composition on the bottom anti-reflective coating film; (c) exposing the resultant structure; (d) baking the resultant structure; and (e) developing the resultant structure to obtain ultra fine patterns.

[0023] As described above, when photoresist has high absorbance to light source, the amount of light reached on an upper portion of photoresist is larger than that of a lower portion. Therefore, when a chemically amplified photoresist is used, the amount of acid on the upper portion of photoresist, generated by acid generator included in photoresist, becomes larger than that of the lower portion. As a result, sloping patterns may be formed as shown in FIG. 1b.

[0024] In order to overcome this problem, an excessive amount of an acid generator is added in a bottom anti-reflective coating composition. Acid generated from the acid generator is diffused in photoresist to supplement acid in a lower portion, thereby obtaining vertical patterns.

[0025]FIG. 1c is a cross sectional view of the pattern formation obtained in the present invention. A bottom anti-reflective coating film 200 containing acid generator is coated on an underlying layer 100, and a photoresist 102 is coated thereon. As a result, vertical patterns are obtained. Due to the photoresist 102 having high absorbance to light source, although the amount of light reached on the upper portion of the photoresist 102 is larger than that of the lower portion, acid A generated from the acid generator included in the bottom anti-reflective coating film 200 is diffused into the photoresist 102 to supplement acid formed in a lower portion, thereby obtaining vertical patterns 104.

[0026] A bottom anti-reflective coating composition of the present invention comprises an excessive amount of photoacid generator or thermal acid generator, more preferably, photoacid generator or thermal acid generator; a compound of Formula 1 as curing agent; polyvinylphenol of Formula 2, serving as photo-absorbent, as base resin; and organic solvent:

[0027] wherein R₁ and R₂ is linear or branched C₁-C₁₀ alkyl, and R₃ is hydrogen or methyl;

[0028] It is preferable that the compound of Formula 1 is selected from the group consisting of Formulas 1a to 1d:

[0029] Any of conventional photoacid generator, which is able to generate acids when it is exposed to light, can be used. Some of conventional photoacid generators are disclosed in U.S. Pat. No. 5,212,043 (May 18, 1993), WO 97/33198 (Sep. 12, 1997), WO 96/37526 (Nov. 28, 1996), EP 0 794 458 (Sep. 10, 1997), EP 0789 278 (Aug. 13, 1997), U.S. Pat. No. 5,750,680 (May 12, 1998), GB 2,340,830 A (Mar. 1, 2000), U.S. Pat. No. 6,051,678 (Apr. 18, 2000), GB 2,345,286 A (Jul. 5, 2000), U.S. Pat. No. 6,132,926 (Oct. 17, 2000), U.S. Pat. No. 6,143,463 (Nov. 7, 2000), U.S. Pat. No. 6,150,069 (Nov. 21, 2000), U.S. Pat. No. 6,180,316 BI (Jan. 30, 2001), U.S. Pat. No. 6,225,020 B1 (May 1, 2001), U.S. Pat. No. 6,235,448 B1 (May 22, 2001) and U.S. Pat. No. 6,235,447 B1 (May 22, 2001). The photoacid generator is present in an amount ranging from 0.1 to 20 wt % of the gross weight of base resin and curing agent, preferably from 0.1 to 10 wt % of the gross weight of base resin and curing agent.

[0030] However, sloping patterns may result when the photoacid generator is present in an amount of below 0.1 wt %, and patterns may collapse when the photoacid generator is present in an amount of over 20 wt %.

[0031] The photoacid generator is selected from the group consisting of diphenyl iodide hexafluorophosphate, diphenyl iodide hexafluoroarsenate, diphenyl iodide hexafluoroantimonate, diphenyl p-methoxyphenylsulfonium triflate, diphenyl p-toluenylsulfonium triflate, diphenyl p-tert-butylphenylsulfonium triflate, triphenylsulfonium hexafluoroarsenate, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium triflate, dibutylnaphthylsulfonium triflate, phthalimidotrifluoromethane sulfonate, dinitrobenzyltosylate, n-decyl disulfone, naphthylimido trifluoromethane sulfonate and mixtures thereof.

[0032] Any of conventional thermal acid generator, which is able to generate acids when it is exposed to heat, can be used. Particularly, it is preferable that the thermal acid generator is selected from the group consisting of Formula 3, Formula 4 and mixtures thereof:

[0033] wherein A is a sulfonate group. Here, it is preferable that the A is

[0034] wherein is 0 or 1.

[0035] The thermal acid generator is present in an amount ranging from 20 to 100 wt % of the gross weight of base resin and curing agent, preferably from 30 to 50 wt % of the gross weight of base resin and curing agent.

[0036] However, sloping patterns may be obtained when the thermal acid generator is present in an amount of below 20 wt %. When the thermal acid generator is present in an amount of over 100 wt %, the thermal acid generator is decomposed during the high thermal process, thereby generating residue on a hot plate.

[0037] In other words, the thermal acid generator exceeds in its amount because the thermal acid generator of the present invention is further added in the conventional bottom anti-reflective coating composition.

[0038] It is preferable that the compound of Formula 3 is represented by Formula 5, and that the compound of Formula 4 is represented by Formula 6:

[0039] It is preferable that the compound of Formula 5 is selected from the group consisting of Formulas 5a to 5d, and that the compound of Formula 6 is selected from the group consisting of Formulas 6a to 6b:

[0040] Any of conventional organic solvent can be used. Some of conventional organic solvents are disclosed in U.S. Pat. No. 5,212,043 (May 18, 1993), WO 97/33198 (Sep. 12, 1997), WO 96/37526 (Nov. 28, 1996), EP 0 794 458 (Sep. 10, 1997), EP 0789 278 (Aug. 13, 1997), U.S. Pat. No. 5,750,680 (May 12, 1998), GB 2,340,830 A (Mar. 1, 2000), U.S. Pat. No. 6,051,678 (Apr. 18, 2000), GB 2,345,286 A (Jul. 5, 2000), U.S. Pat. No. 6,132,926 (Oct. 17, 2000), U.S. Pat. No. 6,143,463 (Nov. 7, 2000), U.S. Pat. No. 6,150,069 (Nov. 21, 2000), U.S. Pat. No. 6,180,316 B1 (Jan. 30, 2001), U.S. Pat. No. 6,225,020 B1 (May 1, 2001), U.S. Pat. No. 6,235,448 B1(May 22, 2001) and U.S. Pat. No. 6,235,447 B1 (May 22, 2001). Preferred organic solvents for the photoresist composition include methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, propylene glycol methyl ether acetate, cyclohexanone, 2-heptanone, ethyl lactate or mixtures thereof.

[0041] There is also provided a semiconductor device manufactured according to the disclosed process for forming patterns as described above.

[0042] The disclosed process for forming patterns using bottom anti-reflective coating film will now be described in more details by referring to examples below, which are not intended to be limiting.

Example 1 Measurement of Absorbance of Photoresist

[0043] DHA1001 photoresist [Dongin Semichem Co.] was coated at a thickness of 1 μm on a quartz substrate, baked at 130° C. for 90 seconds, and then cooled at 23° C. The coated photoresist measures 46% in permeability via JASCO VUV 200 spectrometer.

Example 2 Preparation of Curing Agent Included in Organic Bottom Anti-Reflective Coating Composition

[0044] Acrolein (10 g), THF (66 g) and AIBN (2 g) were added into a flask having round bottom (500 ml). In vacuum state, the resulting solution was reacted at a temperature of 65° C. for 5 hours. After reaction, a generated white solid (poly acrolein) was filtered, and then repeatedly washed with ethyl ether (yield 80%). After the white solid (80 g) and methanol (500 g) were added into a flask having round bottom (1000 ml) and trifluoromethyl sulfonic acid (1 ml) used as catalyst was also added therein, the resulting solution was reacted at room temperature for about 24 hours. The white solid (poly acrolein), which had not been dissolved at the initial stage, was dissolved in methanol as the reaction was completed. When it was confirmed that absorption band of 1690 cm⁻¹ disappeared after completion of the reaction in IR spectrum, the resulting solution was neutralized with triethylamine and then methanol therein was removed using distiller. When the resulting solution was turned into thick state, precipitation obtained from distilled water was vacuum-dried to obtain the compound of Formula 1a (yield 65%).

[0045] molecular weight 6,820; polydispersity 1.60;

[0046]¹H NMR 1.2˜2.1 ppb(3H), 3.0˜3.8 ppb(6H), 3.8˜4.7(1H).

Example 3 Preparation of Organic Bottom Anti-Reflective Coating Composition (1)

[0047] To 24.7 g of propyleneglycol methyletheracetate was added the curing agent (0.26 g) of Formula 1a obtained from Example 2 and the polyvinylphenol (0.455 g) of Formula 2. Here, the thermal acid generator (0.2 g) of Formula 5a was added, dissolved and then filtered using fine filter of 0.2 μm to obtain an organic bottom anti-reflective coating composition.

Example 4 Preparation of Organic Bottom Anti-Reflective Coating Composition (2)

[0048] To 24.7 g of propyleneglycol methyletheracetate was added the curing agent (0.26 g) of Formula la obtained from Example 2 and the polyvinylphenol (0.455 g) of Formula 2. Here, the thermal acid generator (0.3 g) of Formula 6a was added, dissolved and then filtered using fine filter of 0.2 Ξm to obtain an organic bottom anti-reflective coating composition.

Example 5 Preparation of Organic Bottom Anti-Reflective Coating Composition (3)

[0049] To 100 ml of organic bottom anti-reflective coating composition (Clariant 1C5D) was added the thermal acid generator (0.2 g) of Formula 5a, and dissolved to obtain an organic bottom anti-reflective coating composition.

Example 6 Preparation of Organic Bottom Anti-Reflective Coating Composition (4)

[0050] To 100 ml of organic bottom anti-reflective coating composition (Clariant 1C5D) was added the thermal acid generator (0.7 g) of Formula 6a, and dissolved to obtain an organic bottom anti-reflective coating composition.

Example 7 Preparation of Organic Bottom Anti-Reflective Coating Composition (5)

[0051] To 100 ml of organic bottom anti-reflective coating composition (Clariant 1C5D) was added the photoacid generator, triphenylsulfonium triplate (0.2 g), and dissolved to obtain an organic bottom anti-reflective coating composition.

Example 8 Preparation of Organic Bottom Anti-Reflective Coating Composition (6)

[0052] To 100 ml of organic bottom anti-reflective coating composition (Clariant 1C5D) was added the photoacid generator, diphenyl iodide hexafluoroantimonate (0.2 g), and dissolved to obtain an organic bottom anti-reflective coating composition.

Example 9 Formation of patterns (1)

[0053] The organic anti-reflective coating composition obtained from Example 3 was coated on a substrate at a thickness of 400 Å, baked at 220° C. for 90 seconds and then cooled at 23° C. to prepare a substrate having an organic bottom anti-reflective coating film.

[0054] The photoresist used in Example 1 was coated on the substrate at a thickness of 0.40 μm, baked at 130° C. for 90 seconds and then cooled at 23° C. The resultant structure was exposed using ArF exposing device of ASML Co. (PASS/900, NA=0.63), baked at 130° C. for 90 seconds and developed using TMAH aqueous solution of 2.38 wt % to obtain a vertical 120 nm L/S pattern (see FIG. 2).

Example 10 Formation of Patterns (2)

[0055] The procedure of Example 9 was repeated but using the organic bottom anti-reflective coating composition obtained from Example 4 to obtain a vertical 120 nm L/S pattern (see FIG. 3).

Example 11 Formation of Patterns (3)

[0056] The procedure of Example 9 was repeated but using the organic bottom anti-reflective coating composition obtained from Example 5 coated on a substrate at a thickness of 390 Å to obtain a vertical 120 nm L/S pattern (see FIG. 4).

Example 12 Formation of Patterns (4)

[0057] The procedure of Example 9 was repeated but using the organic bottom anti-reflective coating composition obtained from Example 6 coated on a substrate at a thickness of 390 Å to obtain a vertical 120 nm L/S pattern (see FIG. 5).

Example 13 Formation of Patterns (5)

[0058] The organic bottom anti-reflective coating composition obtained from Example 7 was coated on a substrate at a thickness of 390 Å, baked at 200° C. for 60 seconds and then cooled at 23° C. to prepare a substrate having an organic anti-reflective coating film.

[0059] The photoresist used in Example 1 was coated on the substrate at a thickness of 0.30 μm, baked at 130° C. for 90 seconds and then cooled at 23° C. The resultant structure was exposed using ArF exposing device of ASML Co. (PASS/900, NA=0.63), baked at 130° C. for 90 seconds and developed using TMAH aqueous solution of 2.38 wt % to obtain a vertical 120 nm L/S pattern (see FIG. 6).

Example 14 Formation of Patterns (6)

[0060] The procedure of Example 13 was repeated but using the organic anti-reflective coating composition obtained from Example 8 to obtain a vertical 120 nm L/S pattern (see FIG. 7).

Example 15 Preparation of Organic Anti-Reflective Coating Composition Containing a Small Amount of Thermal Acid Generator

[0061] To 24.7 g of propyleneglycol methyletheracetate was added the curing agent (0.26 g) of Formula 1a obtained from Example 2 and the polyvinylphenol (0.455 g) of Formula 2. Here, the thermal acid generator (0.04 g) of Formula 5a was added, dissolved and then filtered using fine filter of 0.2 μm to obtain an organic bottom anti-reflective coating composition.

Example 16 Formation of Patterns

[0062] The procedure of Example 9 was repeated but using the organic anti-reflective coating composition of Example 15 to obtain a sloping 120 nm L/S pattern (see FIG. 8).

Comparative Example Formation of Patterns

[0063] The photoresist used in Example 1 was coated on the substrate coated with organic anti-reflective coating composition (Clariant 1C5D) at a thickness of 0.4 μm, baked at 130° C. for 90 seconds and then cooled at 23° C. The resultant structure was exposed using ArF exposing device of ASML Co. (PASS/900, NA=0.63), baked at 130° C. for 90 seconds and developed using TMAH aqueous solution of 2.38 wt % to obtain a sloping 120 nm L/S pattern (see FIG. 9).

[0064] As discussed earlier, patterns are formed using bottom anti-reflective coating film containing an excessive amount of acid generator. As a result, not sloping but vertical patterns may be obtained because acid is diffused into a lower portion of photoresist from the acid generator included in the bottom anti-reflective composition, although photoresist resins having high absorbance to light source are used, that is the amount of light reached on the lower portion of photoresist is smaller than that of a upper portion. 

What is claimed is:
 1. A bottom anti-reflective coating composition for a semiconductor device comprising a base resin, a curing agent and a solvent, further comprising an acid generator.
 2. The bottom anti-reflective coating composition according to claim 1, wherein the acid generator is a photoacid generator.
 3. The bottom anti-reflective coating composition according to claim 2, wherein the photoacid generator is present in an amount ranging from 0.1 to 20 wt % of the gross weight of the base resin and the curing agent.
 4. The bottom anti-reflective coating composition according to claim 3, wherein the photoacid generator is present in an amount ranging from 0.1 to 10 wt % of the gross weight of the base resin and the curing agent.
 5. The bottom anti-reflective coating composition according to claim 2, wherein the photoacid generator is selected from the group consisting of diphenyl iodide hexafluorophosphate, diphenyl iodide hexafluoroarsenate, diphenyl iodide hexafluoroantimonate, diphenyl p-methoxyphenylsulfonium triflate, diphenyl p-toluenylsulfonium triflate, diphenyl p-tert-butylphenylsulfonium triflate, triphenylsulfonium hexafluoroarsenate, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium triflate, dibutylnaphthylsulfonium triflate, phthalimidotrifluoromethane sulfonate, dinitrobenzyltosylate, n-decyl disulfone, naphthylimido trifluoromethane sulfonate and mixtures thereof.
 6. The bottom anti-reflective coating composition according to claim 1, wherein the acid generator is a thermal acid generator.
 7. The bottom anti-reflective coating composition according to claim 6, wherein the thermal acid generator is present in an amount ranging from 20 to 100 wt % of the gross weight of base resin and curing agent.
 8. The bottom anti-reflective coating composition according to claim 7, wherein the thermal acid generator is present in an amount ranging from 30 to 50 wt % of the gross weight of base resin and curing agent.
 9. The bottom anti-reflective coating composition according to claim 6, wherein the thermal acid generator is selected from the group consisting of Formula 3, Formula 4 and mixtures thereof:

wherein A is a sulfonate group, and n is 0 or
 1. 10. The bottom anti-reflective coating composition according to claim 9, wherein the A is


11. The bottom anti-reflective coating composition according to claim 9, wherein the compound of Formula 3 is represented by Formula 5:

wherein A is a sulfonate group, and n is 0 or
 1. 12. The bottom anti-reflective coating composition according to claim 9, wherein the compound of Formula 4 is represented by Formula 6:

wherein A is a sulfonate group, and n is 0 or
 1. 13. The bottom anti-reflective coating composition according to claim 11, wherein the compound of Formula 5 is selected from the group consisting of Formulas 5a to 5d:


14. The bottom anti-reflective coating composition according to claim 12, wherein the compound of Formula 6 is selected from the group consisting of Formulas 6a to 6b:


15. The bottom anti-reflective coating composition according to claim 1, wherein the curing agent comprises a compound of Formula 1 and the base resin comprises polyvinylphenol of Formula 2:

wherein R₁ and R₂ is linear or branched C₁-C₁₀ alkyl, and R₃ is hydrogen or methyl;


16. The bottom anti-reflective coating composition according to claim 15, wherein the compound of Formula 1 is selected from the group consisting of Formulas 1a to 1d:


17. A process of forming photoresist patterns comprising: (a) coating and baking an organic bottom anti-reflective coating composition on an underlying layer to form a bottom anti-reflective coating film; and (b) forming a photoresist film on the bottom anti-reflective coating film, wherein the bottom anti-reflective coating composition comprises an acid generator.
 18. A process of forming photoresist patterns comprising: (a) forming a bottom anti-reflective coating film by coating and baking the bottom anti-reflective coating composition of claim 1 on an underlying layer; (b) forming a photoresist film by coating and baking a photoresist composition on the bottom anti-reflective coating film; (c) exposing the resultant structure; (d) baking the resultant structure; and (e) developing the resultant structure to obtain ultra fine patterns.
 19. The process according to claim 18, wherein the acid generator is a photoacid generator or a thermal acid generator.
 20. A semiconductor device manufactured according to the process of claim
 18. 